COBALT POWDERS |
|
|
COUF - (CO 7106) |
| Fisher grain size (µm): |
1.60 ± 0.15 |
| Oxygen content: |
Typical 0.65% - Guaranteed 1.0% max. |
| Cobalt content: |
(excluding oxygen) 99.7% min. |
|
 |
Scanning electron microscopy x 5000 (1 cm=2 microns) |
|
|
|
|
COF - (CO 6105) |
| Fisher grain size (µm): |
1.25 ± 0.2 |
| Oxygen content: |
Typical 0.55% - Guaranteed 0.9% max. |
| Cobalt content: |
(excluding oxygen) 99.7% min. |
|
 |
Scanning electron microscopy x 5000 (1 cm=2 microns) |
|
|
|
|
COC - (CO 6101) |
| Fisher grain size (µm): |
1.60 ± 0.15 |
| Oxygen content: |
Typical 0.5% - Guaranteed 0.8% max. |
| Cobalt content: |
(excluding oxygen) 99.7% min. |
|
 |
Scanning electron microscopy x 5000 (1 cm=2 microns) |
|
|
|
|
COD - (CO 6102) |
| Fisher grain size (µm): |
1.8 ± 0.2 |
| Oxygen content: |
Typical 0.4% - Guaranteed 0.75% max. |
| Cobalt content: |
(excluding oxygen) 99.7% min. |
|
 |
Scanning electron microscopy x 5000 (1 cm=2 microns) |
|
|
|
|
COH - (CO 6106) |
| Fisher grain size (µm): |
3.5 ± 0.5 |
| Oxygen content: |
Typical 0.3% - Guaranteed 0.6% max. |
| Cobalt content: |
(excluding oxygen) 99.7% min. |
|
 |
Scanning electron microscopy x 5000 (1 cm=2 microns) |
|
|
|
|
COFS - (CO 6103) |
| Fisher grain size (µm): |
1.40 ± 0.2 |
| Oxygen content: |
Typical 0.8% max. |
| Cobalt content: |
(excluding oxygen) 99.7% min. |
|
 |
Scanning electron microscopy x 5000 (1 cm=2 microns) |
|
|
|
HARDNESS AS A FUNCTION OF SINTERING TEMPERATURE (HOT PRESSING)
|
 |
|